Plastic cracking of concrete.
Read Online
Share

Plastic cracking of concrete.

  • 82 Want to read
  • ·
  • 14 Currently reading

Published by British Cement Association in Slough .
Written in English


Book details:

Edition Notes

Previous ed., 1981.

SeriesBCA guide
ContributionsBritish Cement Association.
ID Numbers
Open LibraryOL17202795M

Download Plastic cracking of concrete.

PDF EPUB FB2 MOBI RTF

Plastic shrinkage cracks are caused by a rapid loss of water from the surface of concrete before it has set. The critical condition exists when the rate of evapora- tion of . CRACKING IN PLASTIC CONCRETE Cracks that form in plastic concrete can be categorised as either plastic shrinkage cracking or plastic settlement cracking. Both of these types result from the bleeding and segregation process that occurs when fresh concrete is placed. Such cracks usually appear from one to six hours after concrete Size: KB. Plastic shrinkage cracking is a mechanical phenomenon that occurs in the first few hours after casting the concrete in its mould. It is commonly believed that rapid and excessive moisture loss of Author: Faez Sayahi. plastic. These cracks appear mostly on horizontal surfaces. They are usually parallel to each other on the order of 1 to 3 feet apart, relatively shallow, and generally do not intersect the perimeter of the slab. Plastic shrinkage cracking is more likely to occur when high evaporation rates cause the concrete surface to dry out before it has Size: KB.

water is transported to the concrete surface will impact the potential for the phenomenon or form of cracking commonly referred to as plastic shrinkage cracking. It has been reported that if the rate of surface evaporation exceeds about Ib/ft 2/h ( kg/ m /h), the loss of moisture may exceed the rate at which bleed water reaches the surface,File Size: KB. Publisher Summary. This chapter introduces a book that focuses on the fracture mechanics of structural concrete. The book aims to discuss the latest developments in computational theories on multiple-crack analysis and mixed-mode fracture in structural concrete and the application of these theories to solve important engineering problems. Where plastic settlement cracking is apparent in the newly placed concrete, the most effective way of eliminating their occurrence is to re-vibrate the concrete after the cracks have formed but before initial set. Assessing the most appropriate time is the responsibility of the operative. Shrinkage cracks occur while the concrete is curing and can be reduced or prevented with proper joint placement. Settlement cracks happen when the ground beneath the slab wasn't compacted properly and part of the concrete sinks. Structural cracks wider than a credit card, or that run through the entire slab require repair or replacement of the concrete. ACCEPTABLE CRACK WIDTHS.

  2. Plastic Settlement Crack. Plastic settlement crack is commonly confused with plastic shrinkage crack due to its almost similar behavior, it can be also seen on the slab. It usually appears between 10 minutes to 3 hours after pouring the concrete. You might ask, why this Plastic Settlement Crack . What is plastic cracking in concrete? This term refers to cracking which occurs while the concrete is still in a plastic state. The phenomenon is most common in hot, dry climates and can usually be attributed to settlement of the mix in the form or over-rapid drying. Cracks and Crack Control in Concrete Structures Fritz Leonhardt Professor Emeritus Dr.-Ing. Dr.-Ing. h.c. mull. Consulting Engineer Stuttgart, FRG The material presented in this paper is based on more than 30 years of re-search, observations and experience concerning causes, control, and conse-quences of cracking in concrete Size: 2MB. This NRA BA 24 standard covers Early Thermal Cracking of Concrete, and shall only be used as referenced from an Assessment Standard contained within Section 4 of Volume 3 of the NRA DMRB. Annex A - BA 24/87 Early Thermal Cracking of Concrete Annex A contains BA 24/87 Early Thermal Cracking of Concrete.